When measuring mold temperature, where do you apply the probe? Side of the blocks? In the cavity?
I’m about to embark on building a block oven and need to figure some things out.
When measuring mold temperature, where do you apply the probe? Side of the blocks? In the cavity?
I’m about to embark on building a block oven and need to figure some things out.
i don't belive that mold temp tells you much. i never did it. i warm the mold, cast a few molds full. by then, the bullets are filled out. when they are; i keep a steady cadence. my bullets weight +- .1 (1 tenth) some a very little more. don't know what the mold temp is and don't care. some molds cast hotter or cooler than others. i do have a pot thermometer.
I agree that maintaining whatever temp your mold casts your alloy well is a matter of maintaining a cadence that works for the alloy temp and environmental conditions you’re working with. I find that happens around 400° F for my molds, and a K-type thermocouple in one of the cavities while the mold prewarms (or rewarms: I find it challenging to maintain a perfect cadence) lets me hit that on the nose from the first pour.
P.I.D.'s, one for the pot and one to rotate with the powder coating oven or mold heater.
Slim
JUST GOTTA LOVE THIS JOINT.
Much depends on the cast profile, whether HP or solid & whether long slender rifle or fat pistol cast.
I've found that a 300º ~ 350ºƒ preheat temperature on the mould will get you good casts in the first or second casting. Having your pot stable at 715º ~ 750ºƒ is a good place for both profiles & the cadence will keep the mould at a steady temperature.
I think drilling the mould for a thermocouple temp. reading is a bit over the top...excessive effort. A good hot plate with a proper setup, skill saw blade and gallon size tin can with a BBQ analogue thermometer is about as simple & dependable as it gets.
a m e r i c a n p r a v d a
Be a Patriot . . . expose their lies!
“In a time of deceit, telling the truth is a revolutionary act.” G. Orwell
If you set the cold mould with handles attached, on top of cold alloy in the pour pot, then turn the pot on. When the alloy is ready to cast so is the mould. You just put through about six rotations, pour, drop, pour dumping the bad bullets and sprue into the sprue box and the top of the mould gets hot enough to cast keepers top to bottom.
Cold mould and hot alloy does not work.
“There is a remedy for all things, save death.“
Cervantes
“Never give up, never quit.”
Robert Rogers
Roger’s Rangers
There are three kinds of men. The one that learns by reading. The few who learn by observation. The rest of them have to pee on the electric fence for themselves.
Will Rogers
In the cavity is what I do. On top of hot plate with aluminum plate to distribute heat. When it reaches 400’ start casting. Maintain cadence, Then set ingots on top of aluminum plate, to start warming, so pot temp. Stays up when refilling. Also wear gloves , or pick up with channel locks But be careful those hot plates can and will melt alloy. Ask me how I know.
"The strongest reason for the people to retain the right to keep and bear arms is, as a last resort, to protect themselves against tyranny in government..... When the people fear their government there is tyranny, when the government fears the people, there is liberty." Thomas Jefferson
Generally my testing method is unintendedly done utilizing my thumb on the sprue plate, if it hurts but doesn't leave a mark it's too cold it it leaves a brand is generally just right.
Otherwise its just a preheat on #3/4ish on my Wally world hot plate and start casting till (if ever depending on the mould/cavities) I start getting frosted bullets or i run the pot down on lead. I dont really have a mould target temp prior to casting.
I did figure out this weekend that the temp control on my Wally World hot plate went out and now has one setting when plugged in (always on full) and the mould I was warming was definitely on the HOT end
Perhaps someday if i get more organized and consistent on what lead is in the pot I may make some notes on alloy, temp and mould for that session, however being that through seems too much like work to me.
~~~~~~~~~~~~~~
“If someone has a gun and is trying to kill you, it would be reasonable to shoot back with your own gun.”
― The Dalai Lama, Seattle Times, May 2001
Hey Jtarm
Although you will be scoffed at by many, I am sympathetic to your quest to go beyond "Good Enough for me". Temperature control is a temperamental bitch. Monitoring can also be somewhat dodgy. Single cavity moulds present fewer variants and are easier to keep in control. The various materials employed also eliminate across the board universal answers. The original question posed is "How do you measure mold temp". OK here goes.
Fluke, double pickup, K type thermocouple, 4" probe and C type surface contact. CME, quick change, mid range direct connect couple. DMS, quick change, mid range, L type thermocouple with magnetic ceramic pickup. Mypin averaging SSR, K type thermocouple, 4" probe. The points of monitoring are, alloy reservoir, mould exterior, mould interior, pot spout, heat sink used for mould cooling. It can become tedious to keep up with it all. An assistant is an invaluable aid in monitoring and recording the multitude of data. To become a competitive shooting champion, many things must be pushed to greater levels than "Good Enough".
Good skill to you.
Roy
Shoot often, Shoot well.
Sprue late temp is more important. If the plate is up to temp, mold is also.
Whatever!
I was also wondering how many 12V power pacs it took to run the hot plate..... sorry... couldn't help it...
Serious question.... I never thought about covering the hotplate with an enclosure... do you find that it heats up the sprue plates as well?
Even if I heat my mold, I have to mallet the plate open for the first 8 or so casts, until it gets hot enough to push open by hand... That would be a good thing if the can enclosure eliminated that...
edit: and I agree, more is always better.... except for traffic... more is not better with traffic...
I don’t measure any temperatures. I’ll put a mold on top of the pot and when the alloy is melted, I start casting watching how the boolits turn out. I use the method of heating the alloy until the boolits start to frost and then back off the heat a bit. If the sprue looses it’s normal shape and gets thin, then I know that the mold is too hot.
I have a saw blade laying on a burner plate. I turn it up until my temp gun says the blade is in the 300-350 range. I lay the mould on top. I hit it with a temp gun. When its anywhere from 280 or over, and my melt is up to temp (PID), I start.
Don't think it matters that much where in the block you drill. Probably depends on size of mould as much as anything. Mine are all 2 cavity and this worked for me. That's just a q-tip in there for clarity and there's a set screw to secure it too. I have also used the flat surface K but the probe works just fine.
Long as we're rambling on I built an insulated "hut" to sit the mould in and my opinion is that unless you're casting OUTSIDE in the open air they're not going to speed any heating up process of the mould and they're nuisance in the bargain.
Should add to avoid the cavity area to this. Otherwise just the front or side of the block whichever is handier for your setup.
Last edited by Mike W1; 03-24-2023 at 01:27 PM.
Mike
Benefactor Member NRA
Life Member Iowa Firearms Coalition
US Army Vet
There are two ways to conquer and enslave a nation.
One is by the sword. The other is by debt.”
John Adams 1826
the way I test mold temp is when the bullets start coming out well formed and shiny or frosty i quit putting them back into the melting pot and pile them up in a towel lined basket ready to be lubed
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |