On another forum I mentioned that we always try to stay away from zinc when casting bullets but now that we are powder coating our bullets perhaps there's a way to use zinc to our advantage. I've never seen this discussed anywhere so I thought I would bring it here & see if some you guys that might know a bit about blending metals, etc. We know that zinc has a much higher melting point but if we go there and alloy the zinc with our other metals can we make a good cast bullet? With powder coating maybe there is a way we can keep from throwing away some of the zinc & use it as a hardener & make good bullets by powder coating them, what say you?
Dick