I have searched and read everything I can find about powder coating boolits and could not find an answer to this question:
Can I use powder coating to increase the diameter of a boolit?
How much can I expect to gain?
Thanks if you can help.
I have searched and read everything I can find about powder coating boolits and could not find an answer to this question:
Can I use powder coating to increase the diameter of a boolit?
How much can I expect to gain?
Thanks if you can help.
Yes.......check out the Coatings and Alternatives. Better to start a thread over there as there will be more eyes looking at your post. I did some powder coating a few months back but I can't remember right of hand how much it added. Over .001 I do know though.
Thanks Rob S ................. and please accept my apologies as I did not know that forum existed.
Sorta.
1 coat of pc from espc is about .001 if a inch.
If you use the BB tumble coat it will be typically be thicker than ESPC
http://castboolits.gunloads.com/show...powder-coating
- and you can do multiple coats if you have too.
How much are you trying to add?
je suis charlie
It is better to live one day as a LION than a dozen days as a Sheep.
Thomas Jefferson Quotations:
"The strongest reason for the people to retain the right to keep and bear arms is, as a last resort, to protect themselves against tyranny in government."
ESPC will get you 0.001 all around which equals 0.002 total increase.
BBDT will CAN get somewhat thicker, depending on how/where you do it.
I shoot my 9mm NLG boolits that are PC'd and then sized in my 38SPL guns all the time with excellent performance. They slip the thru the .358 sizing die and conform the PC perfectly....and load in the brass well too!
banger
Thanks for the replies guys.
I need .002 increase in diameter so it looks doable.
Now to just figure out what ESPC and BBDT mean
Electrostatic (with a powder coat gun) or dry tumble in a staticky plastic container.
Yes it does. I have some 32 cal bullets that were dropping at .311 and I shoot them coated and unsized at .313.
get a candle and a lid of powder. heat,dip etc build it up like a candle. would probably behave similar to saboted?
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |