I have had several Lee 6 Cavity molds. Each one was a PITA in some way. They were my first molds but I even tried one after I started using Lyman. It was a steep learning curve for me. Anyway, I have two Lee 2 Cavity molds. I use bullplate and they work fine. No galling, no smearing. They get up to temp quick and cast fast (for a 2 cavity).
My 6 Cavity were always smearing lead, galling the sprueplate. Stuff like that. Is Bullplate that good for Lee Molds. Was there something else I was doing wrong. I really like Lee 125gr 2R mold for 9mm. I would love to have a 6 cavity lee that works. It cast a lot of bullet fast, you don't have to oil them. I still want one and every time I try one they drive me nuts. Any ideas, what perhaps I was doing wrong.