357 Max:
Michael read alot of your posts on lubs and have put your lubs on my lubs file as lubs to make. My question to you I have been making my wallet quite light with all the great group buys (moulds)
Me too been reading the GB on the alox really haven't used it much. I understand you like to max out your loads and that takes things to just right ie: Lube, aloy, size, and powder ect.
I have found that good barrels/ fat boolits/gas checks/good stiff lube will allow you to do most of what you want....I do not seem to have many problems with most anything...YMMV The question do you use alox in alot of your other lubes and find it valueable item. I have been making FWFL and very pleased with it (Thanks Felix).
I like felix lube..I make mine a little harder though....but alox 606(LLA) and alox 350 are two totally differnet things....alox 350 is a vaseline cosmoline type soapy grease and does not harden or dry I find making lubs quite enjoyable and makes the casting endevor a hobby as well as a componant and knowing I did it myself rewarding.
Me too, I use LLA mostly on less demanding things like 38/32 revolvers...I have and will use it on higher intensity rounds, but it is a PER application type thing....IE ...I use it when the gun likes it...if not....not
Now I don't like to pass on a good deal wich the alox GB is. But sometimes a good buy with minmal use isn't. I might point out that I have about 6 Bottles of the old LLA had it for quite a few yrs.
How often do you use LLA in your lubs.
When it is the right thing to do, and on most things I have had very little trouble, but I have sooooooo much wax based lube I try to use that plus I do not have to wait for it to dry....all in all...my feelings are lube is lube as long as it is a good lube and only your toys can tell you that...I hear of people having this trouble and that trouble all the time....I just must be one lucky devil as I do not seem to have very many troubles.. I seem to have similar shooting as you and would like some input.
Anyone else feel free to give input
Thanks
Don
Anyone else please chime in with some input.