My rifle mold casts bullets just shy of .312" using a mix of 1 part pure lead and 6 parts linotype. My question is, would it fill out the same using COWW or 1-20 alloy? If not, how much difference would I see?
My rifle mold casts bullets just shy of .312" using a mix of 1 part pure lead and 6 parts linotype. My question is, would it fill out the same using COWW or 1-20 alloy? If not, how much difference would I see?
"fill out" as in crisp sharp edges of the cast bullet?
"Fill out" as in cast a larger diameter?
http://www.lasc.us/CastBulletNotes.htm
Scroll down page, on left hand side....bullet shrinkage.
You may lose 1/2 a thou with COWW, but all that depends on alloy composition. I have found that coww is very good for everything that I load. I have plenty of lino, but never use it.
The amount of antimony in the alloy is the largest factor on bullet diameter. Reduce the amount of antimony in the alloy, you reduce as cast diameter. Just like mentioned in post #3.
If you are looking for a larger diameter, you might try Beagling the mold.
I size to .310".
you should be fine .312 down to .310 is ok
If you want it larger, powder coat will add over a .001. I have used 2 coats of powder to use the 30 cal boolit in a mosin nagot.
There is no difference between communism and socialism, except in the means of achieving the same ultimate end: communism proposes to enslave men by force, socialism—by vote. It is merely the difference between murder and suicide. Ayn Rand
Casting cooler alloy reduces shrinkage too.
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |