First Cast Session - Lee 6 Cavity 401-175-TC

[Cast10]

Just finished my first ever casting session. I’m Hooked!

Had some heat issues for a short while but overall cast 420 boolits. Heat added some nice wrinkles to the boolits as well as ‘wings’ on some.

Thanks again for all the info here and help along the way! One and all!

First batch of Boolits cast:



Some wrinkles/lines in bullets:

[Bull-Moose]

Not bad at all. Keep at it, and you will get better.

[G. Freeman]

Wow, those are very nice looking bullets. May I ask what type of lead did u use? Good job, btw.

[pworley1]

It looks like you are off to a good start.

[Mk42gunner]

Good we hooked another one.

I've said it before, but those look a whole lot better than my first few efforts.

Congratulations, now you are no longer stuck with what is available on the shelf.

Robert

[Cast10]

Wow, those are very nice looking bullets. May I ask what type of lead did u use? Good job, btw.

I acquired some SOWW’s from local shop and bought some Hardball from Rotometals. Mixed one 5.25lbs bar of Hardball with 7lbs SOWW’s. This was about 1% SN and 2.5% SB.

[Cast10]

Mk42gunner - Maybe you didn’t have all the ONLINE help like I did, back when you started; just guessing.

The articles here are INVALUABLE! I’ve received so much help and motivation! Thank you all and Tater!

[popper]

Don't stutter on your pour - wrinkles will go away.

[lightman]

That looks like a good start. Much better than my first attempt! Another time to two and your reject pile will be much smaller.

[Cast10]

Popper - Yessir. I’ve learned that the Lee 6 cavity likes to be quick.

[Cast10]

Lightman - After I got the heat issue resolved, I just cooled it down a bit with some fresh fish! Hehe. Picked up the pace a bit and recast the rejects. From that point on I was good to go! Hopefully I can remember that next time! HEHE.

[ACC]

Just finished my first ever casting session. I’m Hooked!

Had some heat issues for a short while but overall cast 420 boolits. Heat added some nice wrinkles to the boolits as well as ‘wings’ on some.

Thanks again for all the info here and help along the way! One and all!

First batch of Boolits cast:



Some wrinkles/lines in bullets:

My 40 S&W SD 40 loves that bullet with most going into 1.5 inch at 30 meters.

ACC

[Cast10]

Nice to hear! I got a 10mm G20 and a MechTech carbine upper. Pig Popper.

[marek313]

Keep that mold hot that will get rid off wrinkles. If your getting fins or "wings" your mold is not closing all the way might be tin collecting at some spots or you just not holding it close. Wait extra second or two longer before you open your mold and you wont get those craters where sprue plate cuts. Those should be nice and flush.

Again there is nothing wrong with a good ole Lee 6 banger. I use the same mold for my 10mm and it works well. Good job and yes casting is very addicting as you see.

[Cast10]

Keep that mold hot that will get rid off wrinkles. If your getting fins or "wings" your mold is not closing all the way might be tin collecting at some spots or you just not holding it close. Wait extra second or two longer before you open your mold and you wont get those craters where sprue plate cuts. Those should be nice and flush.

Again there is nothing wrong with a good ole Lee 6 banger. I use the same mold for my 10mm and it works well. Good job and yes casting is very addicting as you see.

Thanks! I believe you called it correctly. I found myself at the start sometimes holding the sprue cutter handle instead of the other mold handle. Shhhhh! Don’t say anything! Haha. I was guilty as charged for just a few and caught myself. Copy that on the wait a second or two more....I did and most all later on came out smooth. I’ll keep that in mind!

[Tar Heel]

Looking good! Nice bullets.

[Cast10]

Looking good! Nice bullets.

Thank you sir!

[gwpercle]

They Look pretty , real pretty ... but can they shoot ?
OK ... time to make some Gunsmoke ... Choot Em !
Gary

[Cast10]

That’s the plan!

[AndyC]

Very nice indeed - will you be using wax lube or coating them?