Annealed some 44 magnum brass using candle & my sponge method. The very old, fired many times R-P Remington brass has started splitting in the body. Most splits are at mouth from many crimps.
More of a test then anything else. Heat for 30 seconds in flame may have only stress relieved the brass?
The wet sponge keeps the case head from over heating. Very dirty. Lots of black carbon black, but cleans up ok.
Test firing next week, weather permitting. 250 gr lswc & 10. 2 grs Unique. WLP.
Can a candle burn hot enough to anneal brass?
Cognitive Dissident
Temperature + time. Google 2500F. I have done 223 & 6.5 Creedmore. Seems to work when remaining brass has stops splitting at necks. https://www.thehighroad.org/index.ph...oading.909184/
The 44 mag may not anneal, as the wet sponge acts as a heat sink. At 400F brass is stress relieved.
When the water in the sponge starts to sizzle/boil, brass is done .
Last edited by 243winxb; 11-20-2022 at 08:23 AM. Reason: When the water in the sponge starts to sizzle/boil, brass is done .
for what it's worth I have been salt bath annealing my 357/44 mag brass. I wallowed out a couple old n abused Lee molds to serve as heat sinks. Seems to work in that regards but have not cycled them enough to determine if I am mitigating the split mouths or not. This is brass I've been using since the mid-80s (Federal and R-P).
“Some people spend an entire lifetime wondering if they made a difference in the world. But, the Marines don't have that problem.” Ronald Reagan
Now THAT is clever. What do you melt the salt in?
Cognitive Dissident
Decided to build a PSA Dagger, a modified clone of the Glock 19 gen 3. So did a few advances on the gen 3, trigger, sights, etc. Need to run a throating reamer in the SAMMI chamber to taper the lands a bit.
Loaded some 115 ASP J bullet rounds with Unique for initial tests and shoots 1 1/2" not to bad for a compact but not real good either. just so,so. Now loading some 120 RN grain cast with AA #7, see how they do, do not expect to much with the square end lands. If I had a NATO reamer I would run it in.
“There is a remedy for all things, save death.“
Cervantes
“Never give up, never quit.”
Robert Rogers
Roger’s Rangers
There are three kinds of men. The one that learns by reading. The few who learn by observation. The rest of them have to pee on the electric fence for themselves.
Will Rogers
Thanks. I left the cavities small enough for the aluminum to clamp around the brass fairly tight. In the pic they are relaxed and do not show them tight against the brass.
I use a Lee 4 pound pot cranked to the highest setting with a home built PID temp controller. During my last session I was having a bit of difficulty staying at my targeted 925F, so I have pulled the thermostat out of the circuit. Haven't tried it since though. I just liked the idea of having the thermostat in the circuit as a failsafe should the PID decide to go wonky on me. There are a lot of warnings about overheated salts becoming aggressive oxidizers, which I believe is a bad thing!??
I bought the kit from Ballistic recreations several (5?) years ago.
Last edited by oley55; 11-21-2022 at 03:03 PM.
“Some people spend an entire lifetime wondering if they made a difference in the world. But, the Marines don't have that problem.” Ronald Reagan
Of course molten lead has been used for annealing brass and tempering steel for 100 years or more.
Cognitive Dissident
In the absence of a flux to break down the oxide layer, lead won't adhere. Any more than it does to a brass mould.
Cognitive Dissident
A flux is any material (usually liquid) which will bond strongly with the oxygen in the oxide layer on the metal, removing it so as to present a chemically clean brass surface.
Fluxing your lead alloy - same thing. The flux bonds with oxygen strongly enough to cause the oxides in the dross to yield up their metal and let it return to the melt.
If you tinned a mould, my first thought would be that some of whatever you were fluxing your lead with wasn't consumed, and got carried unto the mould. Or possibly some spattered into the mould, if it was close to the pot while you were fluxing your lead.
Fluxes are almost always acids of one kind or another. I'd be amazed if any sort of 2-stroke oil would be acidic.
There's one well known flux which is a gas - hydrogen. I once worked where we brazed GE jet engine parts in a big retort that was flooded with hydrogen, and heated to 1800 degrees. The hydrogen stripped any oxygen off, but left no residue to be cleaned. Managing those retorts was.....interesting. If any air got in before they were fully purged with argon after the heat was done....boom!
Cognitive Dissident
To get away from the dirty candle soot, try using an alcohol burner. Use denatured alcohol from the hardware store.
https://www.amazon.com/Alcohol-Burne...93384489&psc=1
If you want fancy, this popped up in my search. Not sure how it works exactly, but might be the cat's meow for annealing;
https://www.amazon.com/GSC-Internati...93383735&psc=1
Deplorable infidel
I seldom load less than 20g of 2400 in 44Mag and the new brass is definitely softer after firing. By the second firing it's like butter to size. I don't know that annealing is necessary if you have a hot enough load. I've got 3,000 44Mag cases in rotation so it will take me a while to find out. My early brass took about 30 firings to start to split so I'll know in about 90,000 rounds, if I last that long.
Mal
Mal Paso means Bad Pass, just so you know.
A self-annealing load? What a concept!
Cognitive Dissident
Loaded up some Missouri bullet company 165 grain rnfp ( white tail bullets) I’m using 6.5-8.0 grains of red dot. These will be put through my savage 325c. I’ll probably wait untill after deer hunting shoot them. I bought 250 bullets from Missouri bullet company. If the preform well I’ll buy the mold.
Sent from my iPhone using Tapatalk
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |