Hi Guys. Been busy and haven't gotten back to checking on this until now. I did a run of lead bullets (about 14Bnh--mix of linotype and wheel weights) with a Magma Research Bullet Master Mark 5. I...

Confusing post... sorry about that. I guess what I need to consider is that I got a .355 measurement and the other ones were smaller, therefore I need to go with the largest size of .355, go .002...

Update-I slugged my barrel this morning and it ranges from.3535 to .3545. One measurement was .355 but in general the .3535-.3545 seems to be the best average. I checked some of the unresized...

Ok. I will research that info on PC'ing. Thanks.

The first time I tried the epoxy coating it worked fine. No keyholing. I tumbled the bullets in a tub 3 times, letting them dry each time then cooking at 100C for 20-30min in between coats. ...

Thanks for the quick reply 62Chevy! I will slug my barrel as you suggested. I am not getting any leading in the barrel. I water quench as well. Do you think the hardness of ~14BNH is ok?

Just found my original thead was still with comments. I am going to try zinc plated bullets tomorrow or friday. I have been going nuts with lead bullets in 9mm and keyholing so will see if this...

Sorry. This is my Second post....

Hi Guys. I am somewhat new to the forum and this is my first post. I have read all the posts in this forum about the 9mm keyholing problem. My case is the following:
I and two other shooters use...

Hi Guys,
I am a newbie here to Cast Boolits, so apologies if I am repeating what may have been posted on before. I tried searching to find out about this but didn't get a complete answer from...