I can shorten your time, dont bake for 30min, no real point, 15min in a preheated oven is plenty.
Type: Posts; User: fredj338
Forum: Cast Boolits
I can shorten your time, dont bake for 30min, no real point, 15min in a preheated oven is plenty.
Forum: Cast Boolits
Almost impossible to get a mold that throws exactly the correct final size bullet because, as we all know, casting temp & alloy controls final size. Then of course coating adds size too.
Forum: Cast Boolits
Well I dont stand around & breath while baking my bullets, but I know there is a smell, so maybe something in your statement, depending on what powder you use.
Forum: Cast Boolits
Well it depends on your gear. Alox, you are sizing just like PC. With stick lubes, a Lyman/RCBS is pretty slow compared to a Star. I can Alox coat 1000 bullets in maybe 10min. I cant PC in 10min.
Forum: Coatings and Alternatives
PC or Hitek applied properly does not rub of in the sizing die or down the bore. Size after coating. Maybe with a gc I could see sizing first but pb bullets, just extra work for no gain. Sme of my...
Forum: Cast Boolits
A few bores may need 0.358” but i do fine with 0.357” & even my stock glocks will run 0.356”. I do 0.357” fo insurance across several diff guns. I use one coat, baked for 15min. I water drop out of...
Forum: Cast Boolits
Not sure what you mean by tray. There certainly is a time diff but but if sizing both, it might be 1hr more to pc. I can coat & bake 1000 in about an hour, they are then ready to size. What does it...
Forum: Lead and Lead Alloys
Like Forrest I am a wetpack tester. Gel is great but diff to work with. Water is too forgiving of a poor bullet. I like phone books for the convenience but they are going away fast. I still have...
Forum: Lead and Lead Alloys
I used to pay $25 for a 5gal bucket. When the price here went to $50 & almost half was non lead, I quit collecting. If you melt them into 1# ingots, you can flat rate box them for $1/# easy.
Forum: Lead and Lead Alloys
For my LHP I go 20-1 lead/tin for bullets 1000-1300fps. For under 1000fps, 25-1 seems to work well. HP designs can be all over the place though.
Forum: Cast Boolits
If you put enough PC on a bullet to clog the HP, you put on too much.
Forum: Cast Boolits
Ok I'll bite. How do you setup 1000 bullets to PC in 5min??? Reason I dont spray is the bullets need to be all standing then sprayed without knocking them over & theen the waste of powder, but...
Forum: Cast Boolits
I cast about 730-740, alum or steel molds. I often heat molds & ingots on a hot plate. I return sprues to the pot about every 100, Set the mold aside off the heat. It cools a bit while the sprues...
Forum: Cast Boolits
Spoken like someone who hasnt shot many coated. The only downside to coated, PC or HT is time involved. It takes me an extra hour to coat the 1000 bullets. Sizing time is the same using a Lee APP v...
Forum: Cast Boolits
No but I like uniform bullets for loading into mixed brass. Get a thick case & fat bullet, it will be an issue.
Forum: Cast Boolits
I was slow to coated but once I got into it, I wont go back to lubed bullets. They load & shoot cleaner, just as accurate in handguns, less smoke & cost is minimal. Yes they require more time than my...
Forum: Cast Boolits
No but why bother, just toss them. I have manaeged to flux & skim enough at lower temp to remove a lot of zinc contaminates in a pot of alloy. Flux, skim, repeat.
Forum: Cast Boolits
They did it n kommifornia on public lands. They claim it kills birds of prey but anyone that hunts know's that is BS.They just want us to not hunt.
Forum: Cast Boolits
I had one, seemed as accurate as my CabinTree, but not as easy to use, sold it. 99% of my casting pistol ammo. I dont worry that much about bhn.
Forum: Coatings and Alternatives
I bought 1# of the copper. It will shake & bake but use parchment paper underthe bases or put them on their sides.it tends to stick yo bare metal ime. Mixing it with other colors from smoke helps.
Forum: Cast Boolits
I have the opp result with pistol bullets. With more bearing surface, higher pressures & higher vel. With sim bearing lengths & identical powder charges, the smooth bullets are faster.
Forum: Cast Boolits
All my coated bullets have lube grooves because that is what I had before I tarted coating. If I were buying new molds today, I Still would likely opt for grooves. No grooves makes it a unitasker, I...
Forum: Cast Boolits
H110/W296 also doesnt download well. I moved back to 2400 for my magnums. I dont miss the extra 50fps I would get with H110 & gives me more load flexability.
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |