I am old school...really old school. Not a fan of participation trophies etc etc.
Those bullets are awful. You know it, and everyone here knows it. Why would you post something like that?
You may have "studied and studied" but have not learned much.
Information overload is not your problem. The need for instant gratification is your problem.
Go back and try again. Get your mold and alloy so hot that the bullets are frosted then dial temperature back to get perfect bullets. Frosted bullets are good to use so no need to toss them back into the pot. Wrinkled bullets and poor fill are junk.
This is not rocket surgery. Now, if you have contaminated alloy, that will give you a world of hurt. If you cannot get good bullets running hot, buy some decent alloy and try again. There is usually alloy in the S&S section of the forum or you can buy it here:
https://missouribullet.com/results.php?category=12