im shooting a 1-8 and all is good im pushing to the max as i use full loads and some times a bit more to where my brass olny last 6 or 8 reloads and not one had separation happen on the way to the target
i will post a brass round that did not make it built it ded on too load was way to hot
i get rip on for stuff like this but i do testing i will mess up a lot of brass be for testing is over
http://castboolits.gunloads.com/imag...59dc158a43.jpg
/QUOTE]
You are going to hurt yourself or some one else if you keep that up. There is no excuse for working up loads that do that to the brass. You are way past what is reasonable in a production firearm. This kind of stuff is best left to expert facilities who use pressure test barrels and actions with full safety protections in place. When your gun comes apart, and it will eventually, it is likely that it will be more than just the gun that gets damaged. I am not ripping on you, I am pleading with you, don't keep doing this.