405 WCF
01-05-2009, 04:58 PM
This mold will drop bullets from .309 to .312 according to the LEE support.
Cast dia is depending on what alloy used.
Normally, I cast all my bullets with WW+some percent of tin added, but I have a lot of pure lead and linotype that allso can be used.
I have never messured any lino or pure lead bullet, so I dont know how they compare to WW+tin bullets when it comes to cast dia.
The weather is bad here, so, I can not go out and cast some lino or pure lead bullets, just to messure the dia, so now I ask you:
-If I want my mold to drop the top dia bullets, which alloy will give me bullets with the largest dia?
Cast dia is depending on what alloy used.
Normally, I cast all my bullets with WW+some percent of tin added, but I have a lot of pure lead and linotype that allso can be used.
I have never messured any lino or pure lead bullet, so I dont know how they compare to WW+tin bullets when it comes to cast dia.
The weather is bad here, so, I can not go out and cast some lino or pure lead bullets, just to messure the dia, so now I ask you:
-If I want my mold to drop the top dia bullets, which alloy will give me bullets with the largest dia?