Sn

[kbstenberg]

I am able to recycle all of my own lead (I shoot at my own range) Since I always add 1% sn to my alloy, will I have to add additional sn when I remelt my bullets into ingots? I would assume the sn is still in the alloy. But I also know what happens when you assume something.
Kevin

[bumpo628]

You might lose a little to the oxides in the dross, but the majority will be there.

[lwknight]

If you keep adding tin every time , you will eventually have tin bullets with a trace of lead in them.