Mold is NOE 311-242. I don't get it. Is it possible my mold is too hot? I have the mold sitting on a hot plate set to medium. Lead is straight wheel weight set to 700 degrees. Bullet is dropping at .313 at the base. I'm sizing down to .310. I'm attempting to powder coat. The PC isn't coming out perfect but I need to get this stuff fixed first.