Ordered some 99% pure lead.
It didn't come from anyone here or any of the dealers advertised here.
Somethings not right though.
A 400 grain bullet I cast drops 12 grains lighter.
A 262 grain bullet drops 6 grains lighter.
Thats consistently.
When I cut the sprue it breaks like it's brittle.
I have very little trouble using pure lead with just a touch tin.
In general this stuff does not cast well at all.
I would think if it's more tin than I'm used to that fill out would be great.
Thats not the case though.
What do you think?