I have about 100 lbs of #7 shot that has been sitting around for years. Given I don't shot trap anymore, the shot is of no use to me.
So, I have been thinking about melting it down to produce .358 bullets for my S&W 929.
Does anyone know if this will work OK or is there something I should be prepared for?
My immediate worries are;
Will hardened lead shot melt easily in my Lee pot?
Will the bullets be too hard for the intended use?
Any comments or experience you are willing to offer would be greatly appreciated.