As I understand, an alloy with antimony in it will get harder with time. Does it stop at a point?
If you melt an ingot with antimony in it that is thirty years old, will the boolits cast from it be be the same hardness as the ingot after thirty years, or will they revert back to the hardness of the ingot when it was first poured?
Thanks