It seems most people ARE NOT baking PC long enough!!!!
This will cause an incomplete cure which allows gunpowder to affect the PC surface of a bullet and other possible problems.
I've found 2 different bake schedules (which are actually similar with different stages where you start timing the bake cycle
EASTWOOD - Cure Time: 20 Minutes AFTER flowout/the PC melts
PBTP, CARDINAL - 10 minutes AFTER the boolits reach 400°
https://www.powderbuythepound.com/su...wet-black.html
• Cure Schedule = 400f/10 Min at Part Metal Temperature
http://www.cardinalpaint.com/assets/...9-T013-TDS.pdf
Cardinal paint CURE SCHEDULE: (METAL TEMPERATURE) 10 MINUTES @ 400 DEGREES F.
I guess the time is relevant to how/when you start gauging it
https://www.eastwood.com/hotcoat-pow...ight-blue.html
SPECIFICATIONS
Color: Ford Light Blue
Gloss Level: Gloss
Cure Temperature: 400 Degrees
Cure Time: 20 Minutes after flowout