Help identifying partial ingot.

[Dunkem]

Just scored a few chucks of lead. I'm fairly sure it's of the pure-ish variety, a few quick tests prove its dead soft. I can scratch it with a fingernail and when driving a clip on wheel weights into it, the wheel weight will dent it without marking the wheel weight. Just seeing if anybody recognizes the markings and knows anything about it.

Sent from my VS990 using Tapatalk

[pete501]

Pat, I'd like to buy a vowel.
Testing is the only way to know, but if it acts like pure then use it like pure.

[EMC45]

Looks like pure plumber's lead for old oakum joints.

[Grmps]

check simple hardness testing

Casting boolits (lead bullets) properly is a science, once you know the basics, not a hard science.
There is a lot of good information on CB. The Google search (top right of every forum page) is a gateway to all the knowledge on this forum. IF you can’t find your answer there ask the question (Please be as detailed as possible, pictures help http://castboolits.gunloads.com/show...g-screen-shots I would be very surprised if there wasn’t someone on this forum that could answer ANY question you might have)
http://www.lasc.us/Fryxell_Book_Contents.htm
1. Boolits need to be cast .0005 to .003 over the slugged diameter of your barrel for accuracy and to avoid leading. If the fit is wrong nothing else will work right.
a. slugging a barrel (it is safer to use a brass rod or a steel rod with a couple of coats of tape to avoid damaging your barrel http://7.62x54r.net/MosinID/MosinSlug.htm
b. chamber casting https://www.brownells.com/guntech/ce....htm?lid=10614
or pound casting http://castboolits.gunloads.com/show...rifle-chamber)
2. the right alloy needs to be used for the velocity and purpose of the boolit (don’t fall into the trap of going with to hard an alloy
Economical way to easily test lead hardness
http://castboolits.gunloads.com/show...rdness-testing

Some alloys harden over time
http://www.lasc.us/Fryxell_Book_Chap...Metallurgy.htm
different alloy’s different end sizes

Lead alloy calculator
http://castboolits.gunloads.com/atta...4&d=1341560870
3. velocity the bullet needs to be pushed hard/fast enough to get the proper spin, have the proper velocity to accurately reach the target but not so hard as to be dangerous or strip the lead off in the grooves instead of spinning the boolit..
Powders range from fast to slow, you need to choose the right powder for your application.
Loading manuals list the best powders for certain calibers and boolit weights.
NEVER use any posted noncommercial load data without first checking to see if falls in the safe parameter for your firearm!! There are several firearms out there that can handle much higher pressures than others!!
Link to free online load data
http://castboolits.gunloads.com/show...online-sources