Lee PrecisionStainLess Steel MediaADvertise hereMidSouth Shooters Supply
Titan ReloadingInline FabricationRotoMetals2Graf & Sons

Donate Now Goal amount for this year: 6000 USD, Received: 4840 USD (81%)
We have reached our goal! Thanks to all who donated! I will be updating the donation bar in the next few days!
Our Annual server fund drive is going on now! This donation drive helps fund Cast Boolits for an entire year, and helps support our 2nd amendment rights! You can donate by Paypal by clicking the DONATE button. Or by Cash / Check / MO to the address below:

Willy Snyder
PO Box 2732
Pocatello, ID 83206
****Due to overwhelming e-mails, I will be very slow in updating this list. Please bear with me!****


Page 1 of 5 12345 LastLast
Results 1 to 20 of 93

Thread: MP-Molds - 165 grain 40 Caliber 2 and 4 cavity mold - Perfect bullet weight!

  1. #1
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127

    MP-Molds - 165 grain 40 Caliber 2 and 4 cavity mold - Perfect bullet weight!

    This Group Buy is to continue the dialog started by GoodAlloy, and is for a mold to cast 165 grain boolits for 40 cal pistols. That is, both the 10mm and .40 S&W.
    The idea is 165 grains as the solid (the perfect bullet weight), but lighter as hollow point design.

    I have heard back from Miha on the pricing and Powder Coat questions.
    Yes, he can produce your lube groove-LESS molds, but no mixing of lube groove/no lube groove in same mold. The lube groove takes away some weight, so the powder coat/epoxy version of the solid nose will weigh a bit more than the 165 grains. The HP molds will include all three sets of HP pins, per the drawing.

    First, options for mold cavities and prices:

    2 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, Hollow Point, all pins, Brass - 76.50 EUROS, shipped
    2 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, SOLID NOSE ONLY, Brass - 76.50 EUROS, shipped
    4 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, Hollow Point, all pins, Brass - 114.75 EUROS, shipped
    6 Cavity Bullet Lube or Powder Coat style (no lube groove), and no mixing of types in single mold, SOLID NOSE ONLY, ALUMINUM ONLY, 76.50 EUROS, shipped
    Handle, if ordered with your mold, an additional 20 Euros (23 Euros without a mold order)
    These prices are in EUROS, and do in fact reflect the 15% discount for group buys.

    I'm linking my perfect bullet weight comments from one of the following posts, just in case anyone skips over it, and misses the point:
    Discussion about 165 grain being the PERFECT bullet weight for the 40 cal cartridges

    And, here's someone else's take on the subject, with the biggest danger being one of the longer length of the 180 potentially creating dangerous pressures if seated too deeply.
    Another published discussion on why the 165 grain is the best

    We need at least two more HP molds to go active. The sooner it goes active, the faster we will add more orders, and get this one scheduled.

    Here are the drawings we are proposing, On LEFT is the normal boolit. On the RIGHT is the Powder Coat version.
    Click the images for the full sized version:
    Click image for larger version. 

Name:	40 TCHP.jpg 
Views:	85 
Size:	19.5 KB 
ID:	222206 Click image for larger version. 

Name:	40 TCHP PC.jpg 
Views:	43 
Size:	50.3 KB 
ID:	222936

    This is the ORDER list, I need the following:
    * Screen Name
    * How Many molds ?
    * How many Cavities?
    * Lubed (grooved) or Powder Coat style (no grooves)?
    * Gas checked or plain base?
    * Disguised email address
    * Zip Code
    * Handles or no handles?
    * DHL shipping (an additional $7 US) or regular shipping.

    2 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, Hollow Point, all pins, Brass - 76.50 EUROS, shipped
    1) GoodAlloy - (1) two cavity, HP, with all pins, regular lube grooves, gas checked, 43150 Zip Code
    2) rdwarrior- (1) two cavity, normal lube grooves, HP, with all pins, plain base, rdwarrior at charter dot net, 29680 Zip Code (no handles)
    3) georgerkahn - (1) two cavity, HP, with all pins, regular lube grooves, gas checked, no handles, kahngr at potsdam dot edu , 13676 Zip Code
    4) Camper64 - (1) two cavity, powder coat (no grooves), hollow point, all pins, plain base, no handles, regular shipping, DWBoddicker at aol dot com , 52315 Zip Code
    5)
    6)

    2 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, SOLID NOSE ONLY, Brass - 76.50 EUROS, shipped
    1)
    2)
    3)
    4)

    4 Cavity Bullet Lube or Powder Coat style (no lube groove)and no mixing of types in single mold, Hollow Point, all pins, gas checked or plain base, Brass - 114.75 EUROS, shipped
    1) DukeInFlorida - (1) four cavity, HP, Gas Checked, all pins, grooved, DHL shipping, no handles, castboolits at sebagosales dot com, 32127 Zip Code
    2) Minerat - (1) four cavity,, grooved, HP), with all pins, gas checked, 80003 Zip Code
    3) KVO - (1) four cavity, no lube groove, HP, with all pins, Plain Base, bulls (underscore) eye (underscore) 264 at hot mail dot com, 78665 Zip Code (no handles)
    4) bpatterson84 - (1) four cavity, HP, no lube groove, all pins, Plain Base, with handles, rocpyro at gmail dot com
    5) PbHurler - (1) 4-Cavity HP, Brass, normal lube grooves, Plain Base, All Pins, denneyr at sbcglobal dot net, 73099 Zip Code (no handles)
    6) Boomstraw - (1) 4-Cavity HP, Brass, no lube grooves
    7) Highland Drifter - (1) four cavity, no lube grooves, HP, with all pins, plain base, highlander338 at gmail dot com , 84003 Zip Code (no handles)
    8) Tradbear55 - (1) four cavity, HP, Gas Checked, all pins, grooved, bluewrench75 at gmail dot com
    9)
    10)
    11)
    12)
    13)
    14)

    6 Cavity Bullet Lube or Powder Coat style (no lube groove), and no mixing of types in single mold, SOLID NOSE ONLY, ALUMINUM ONLY, 76.50 EUROS, shipped
    1) Loudy13 - (1) 6 cav aluminum, solid nose, no lube grooves
    2) Good Alloy - (1) 6 cavity solid nose, regular lube grooves, plain base, 43150 Zip Code
    3) Good Alloy - (1) 6 cavity solid nose, regular lube grooves, Gas Checked, 43150 Zip Code
    3) RedHawk357Mag - (1) 6 cav solid nose, plain base, regular lube grooves
    4) Hardcast - (1) 6 cav solid nose, plain base, with lube grooves, nclem at ffni dot com, 46920 Zip Code, (no handles)
    5) uaskme - (1) 6 cav solid nose, plain base, with lube grooves, pardue10 at comcast dot net
    6)
    7)

    * marlin39a << Need configuration, etc

    We need at least two more HP molds to go active. The sooner it goes active, the faster we will add more orders, and get this one scheduled.
    Last edited by DukeInFlorida; Yesterday at 05:32 PM.


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  2. #2
    Boolit Man

    Join Date
    Dec 2017
    Location
    Upstate SC
    Posts
    101
    Any chance to make it with HP pins (hopefully penta)?

  3. #3
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    Yes, this mold will be a Cramer style mold, with pin inserts.
    The solid nose pin will yield a 165 grain boolit. We need to discuss what pins you all want.

    Quote Originally Posted by rdwarrior View Post
    Any chance to make it with HP pins (hopefully penta)?


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  4. #4
    Boolit Man

    Join Date
    Dec 2017
    Location
    Upstate SC
    Posts
    101
    I am relatively new to casting (6 months) and just started casting solid boolits for my 40. I am still working on the alloy for my pistol rounds - rifle boolits are working good but I think I need to soften my pistol boolits a little more. With that said I am not sure which pins I should use on this mold. I do have an MP mold for my 357/38 that has round medium and deep HP pins (as well as flat for solids). Thinking from what I have read and seen online the Penta pins work very well.

  5. #5
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    In the Speer Reloading data book #14 , .40 S&W, 165 grain bullets is the following note:
    “Loads marked with approximate law enforcement loads.”

    In much the same way that the 9mm evolved to be a 124 grain bullet for near perfect performance, the 165 grain bullet was evolved to be the perfect 40 caliber bullet weight for law enforcement and military use. Your tax dollars at work. I have a brief article on my web site which covers the details: WEB SITE ARTICLE

    So, this boolit, the 165 grain cast, for the 40 caliber, should prove to be as wonderful as the 124 grain 9mm bullet, and the world renowned H&G #68 for the 45 ACP. I personally plan on running it as a solid nose, rather than a lighter hollow point. Everyone gets all wild eyed about hollow points, including the penta point that rdwarrior mentioned. That's all fine and good. But, remember that the hollow points are lighter than 165 grains. The group buy will be a hollow point with a couple of pin sets.

    I need to get drawings made up, and hope to get that done soon. Suffice it to say, that this mold is destined to become a classic in my opinion. It will get re-run many times over the coming years. I'm delighted to be ushering it into existence, and thankful for the opportunity to be one of the first to cast boolits with it. I get ahead of myself. We need to get some names associated with it, so please..... if you have a .40 S&W that needs feeding, or even a 10 MM, get your name on the interest list. We'll need 25 orders for the hollow point mold. And, we'll need at least 13 names on the interest list before we can launch the official group buy. So, every interested person will help get this classic in the making going!


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  6. #6
    Boolit Master Highland Drifter's Avatar
    Join Date
    Apr 2005
    Location
    Northern Utah
    Posts
    237
    The original interest posted by GoodAlloy was a TC shape that would be 165 grains as a hollow point, and heavier as a solid. Is this going in a different direction? If so than this Lee mold would serve the purpose.
    Click image for larger version. 

Name:	569185.jpg 
Views:	36 
Size:	27.6 KB 
ID:	221932

  7. #7
    Boolit Master

    Join Date
    Apr 2010
    Location
    Oklahoma
    Posts
    756
    Duke,

    Add me to the "watching with interest" group
    Bob

  8. #8
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    Our resident boolit designer informs me that the meplat on the initial GoodAlloy drawing would not have enough meat to support a hollow point. So, yes, it is moving in a slightly different direction. However, what is exciting about the new direction is that we are striving for the PERFECT .40 bullet. One that will historically rival , for example, the quintessential H&H 68 (45acp). A .40 bullet that everyone will talk about in years to come. It will be a 165 grain solid nose.
    I have no argument with casters who choose to cast on Lee molds. However, I don't have any of those in my mold linrary
    They just arent good enough for MY guns. Hope yoi can join us as we create a historical mold.

    Quote Originally Posted by Highland Drifter View Post
    The original interest posted by GoodAlloy was a TC shape that would be 165 grains as a hollow point, and heavier as a solid. Is this going in a different direction? If so than this Lee mold would serve the purpose.
    Click image for larger version. 

Name:	569185.jpg 
Views:	36 
Size:	27.6 KB 
ID:	221932


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  9. #9
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    Added, thanks

    Quote Originally Posted by PbHurler View Post
    Duke,

    Add me to the "watching with interest" group


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  10. #10
    Boolit Master

    FLYCUTTER's Avatar
    Join Date
    Mar 2010
    Posts
    421
    A 165 or 170 gr. 6 cavity solid brass would work for me. Nothing lighter.

  11. #11
    Boolit Master


    Join Date
    Mar 2016
    Location
    MN
    Posts
    314
    I am interested add me, if its available I would be interested in a 6 or 8 aluminum no HP mold if it is available.
    "Yes or no will almost always suffice as the answer"

  12. #12
    Boolit Master
    Join Date
    Mar 2005
    Location
    Indiana
    Posts
    340
    Interested

  13. #13
    Boolit Man


    Herb3's Avatar
    Join Date
    Jul 2011
    Location
    South Carolina
    Posts
    78
    With or without lube groove? I would be interested in 165 to 170 gr solid no lube groove for PC here.

  14. #14
    Boolit Man

    Join Date
    Dec 2017
    Location
    Upstate SC
    Posts
    101
    ok folks we need just 4 more interested folks to move this mold along the way.

  15. #15
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    Lube groove is a standard for those of us who cast and lube. However, I understand that you powder coaters or epoxy coaters want the sides more streamlined. I'd remind you that you can coat any boolit, with or without a groove, and it will perform well. If we removed the groove from this one, it would weigh more than the PERFECT 165.

    However, I will ask Miha if it's possible with the same cherry. I don't think so, but I'll ask.

    Quote Originally Posted by Herb3 View Post
    With or without lube groove? I would be interested in 165 to 170 gr solid no lube groove for PC here.


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


  16. #16
    Boolit Master glockfan's Avatar
    Join Date
    Jan 2018
    Location
    partly VT,partly canada
    Posts
    363
    Quote Originally Posted by Herb3 View Post
    With or without lube groove? I would be interested in 165 to 170 gr solid no lube groove for PC here.


    +1.

    welll.....i'd be interested for a solid 165 grooveless (hi tek) 6 cavities brass mold....so if this can become an option , add me to this discussion thread.

  17. #17
    Boolit Mold
    Join Date
    Dec 2012
    Location
    North Alabama
    Posts
    18
    I am interested. A lighter bullet loaded correctly might be an interesting project.

  18. #18
    Boolit Master

    FLYCUTTER's Avatar
    Join Date
    Mar 2010
    Posts
    421
    Sorry Duke, I'm jumping ship and going to Lakehouse's thread for the 180 gr 40 cal. mold. Please take me off this buy. FLYCUTTER

  19. #19
    Boolit Master Highland Drifter's Avatar
    Join Date
    Apr 2005
    Location
    Northern Utah
    Posts
    237
    I would also be interested in a grooveless 4 cavity h.p. mold for pc. Miha has offered both grooved and grooveless on the same group buy.

  20. #20
    I'm A Honcho!

    DukeInFlorida's Avatar
    Join Date
    Oct 2009
    Location
    East and South of you
    Posts
    3,127
    Sorry to see you go. You could get BOTH, you know. The tax dollars that were spent to figure out that the 165 was the OPTIMUM weight for the 40 S&W were well spent. Do some reading on the subject, and let me know.

    Quote Originally Posted by FLYCUTTER View Post
    Sorry Duke, I'm jumping ship and going to Lakehouse's thread for the 180 gr 40 cal. mold. Please take me off this buy. FLYCUTTER
    Quote Originally Posted by Highland Drifter View Post
    I would also be interested in a grooveless 4 cavity h.p. mold for pc. Miha has offered both grooved and grooveless on the same group buy.
    Still waiting on an answer. Every mold has it's own peculiarities. I'll advise as soon as I get Miha's answer. Thanks for your patience.


    NRA Life Member
    NRA Certified Metallic Cartridge Reloading Instructor

    Author of a book on reloading
    ILSA MEMBER http://www.internationallawnsteelsho...ssociation.com
    NRA RANGE SAFETY OFFICER


Page 1 of 5 12345 LastLast

Posting Permissions

  • You may not post new threads
  • You may not post replies
  • You may not post attachments
  • You may not edit your posts
  •  
Abbreviations used in Reloading

BP Bronze Point IMR Improved Military Rifle PTD Pointed
BR Bench Rest M Magnum RN Round Nose
BT Boat Tail PL Power-Lokt SP Soft Point
C Compressed Charge PR Primer SPCL Soft Point "Core-Lokt"
HP Hollow Point PSPCL Pointed Soft Point "Core Lokt" C.O.L. Cartridge Overall Length
PSP Pointed Soft Point Spz Spitzer Point SBT Spitzer Boat Tail
LRN Lead Round Nose LWC Lead Wad Cutter LSWC Lead Semi Wad Cutter
GC Gas Check