If I cast using straight Linotype, which is what I have. What does the hardness anneal down to after 8 to 12 minutes at 400 degrees?
Also, if I water quench the bullets after their 8 to 12 minutes at 400 degrees, will I regain any of that hardness or is the temp too low?