Like Forrest I am a wetpack tester. Gel is great but diff to work with. Water is too forgiving of a poor bullet. I like phone books for the convenience but they are going away fast. I still have...
Type: Posts; User: fredj338
Forum: Lead and Lead Alloys
Like Forrest I am a wetpack tester. Gel is great but diff to work with. Water is too forgiving of a poor bullet. I like phone books for the convenience but they are going away fast. I still have...
Forum: Lead and Lead Alloys
I used to pay $25 for a 5gal bucket. When the price here went to $50 & almost half was non lead, I quit collecting. If you melt them into 1# ingots, you can flat rate box them for $1/# easy.
Forum: Lead and Lead Alloys
For my LHP I go 20-1 lead/tin for bullets 1000-1300fps. For under 1000fps, 25-1 seems to work well. HP designs can be all over the place though.
Forum: Cast Boolits
If you put enough PC on a bullet to clog the HP, you put on too much.
Forum: Cast Boolits
Ok I'll bite. How do you setup 1000 bullets to PC in 5min??? Reason I dont spray is the bullets need to be all standing then sprayed without knocking them over & theen the waste of powder, but...
Forum: Cast Boolits
I cast about 730-740, alum or steel molds. I often heat molds & ingots on a hot plate. I return sprues to the pot about every 100, Set the mold aside off the heat. It cools a bit while the sprues...
Forum: Cast Boolits
Spoken like someone who hasnt shot many coated. The only downside to coated, PC or HT is time involved. It takes me an extra hour to coat the 1000 bullets. Sizing time is the same using a Lee APP v...
Forum: Cast Boolits
No but I like uniform bullets for loading into mixed brass. Get a thick case & fat bullet, it will be an issue.
Forum: Cast Boolits
I was slow to coated but once I got into it, I wont go back to lubed bullets. They load & shoot cleaner, just as accurate in handguns, less smoke & cost is minimal. Yes they require more time than my...
Forum: Cast Boolits
No but why bother, just toss them. I have manaeged to flux & skim enough at lower temp to remove a lot of zinc contaminates in a pot of alloy. Flux, skim, repeat.
Forum: Cast Boolits
They did it n kommifornia on public lands. They claim it kills birds of prey but anyone that hunts know's that is BS.They just want us to not hunt.
Forum: Cast Boolits
I had one, seemed as accurate as my CabinTree, but not as easy to use, sold it. 99% of my casting pistol ammo. I dont worry that much about bhn.
Forum: Coatings and Alternatives
I bought 1# of the copper. It will shake & bake but use parchment paper underthe bases or put them on their sides.it tends to stick yo bare metal ime. Mixing it with other colors from smoke helps.
Forum: Cast Boolits
I have the opp result with pistol bullets. With more bearing surface, higher pressures & higher vel. With sim bearing lengths & identical powder charges, the smooth bullets are faster.
Forum: Cast Boolits
All my coated bullets have lube grooves because that is what I had before I tarted coating. If I were buying new molds today, I Still would likely opt for grooves. No grooves makes it a unitasker, I...
Forum: Cast Boolits
H110/W296 also doesnt download well. I moved back to 2400 for my magnums. I dont miss the extra 50fps I would get with H110 & gives me more load flexability.
Forum: Cast Boolits
Plenty of time for load development. If air cooled, you might be fine. If water dropping out of the PC oven, you could go a bit softer IMO, maybe 3-1? I cast a sim bullet for my G20, it never shot...
Forum: Cast Boolits
Or too hard for the vel/pressures used.
With proper fit & alloy, a gc isnt needed for most handgun applications. Powder coat, eben less of a reason for nowdays, expensive gc.
Forum: Coatings and Alternatives
I use these, 4 fit perfectly in my pizza oven.
https://m.media-amazon.com/images/I/81v1pyZd-qL._AC_SX679_PIbundle-4,TopRight,0,0_SH20_.jpg
Forum: Cast Boolits
I shoot coated lead, no issues over the labradar.
Forum: Cast Boolits
I think there is diminishing returns going too heavy for caliber. As noted, big bore solids penetrate a lot. A 285gr/45 @ just 1100fps will penetrate more than a 400gr soft @ 2200fps from a 404...
Forum: Cast Boolits
I've got powder 20+, still good. I did have one can of H4831 go bad, no explanation, all stored the same. Leads me to think it was poorly stored before I bought it.
BP | Bronze Point | IMR | Improved Military Rifle | PTD | Pointed |
BR | Bench Rest | M | Magnum | RN | Round Nose |
BT | Boat Tail | PL | Power-Lokt | SP | Soft Point |
C | Compressed Charge | PR | Primer | SPCL | Soft Point "Core-Lokt" |
HP | Hollow Point | PSPCL | Pointed Soft Point "Core Lokt" | C.O.L. | Cartridge Overall Length |
PSP | Pointed Soft Point | Spz | Spitzer Point | SBT | Spitzer Boat Tail |
LRN | Lead Round Nose | LWC | Lead Wad Cutter | LSWC | Lead Semi Wad Cutter |
GC | Gas Check |