I size after i pc. i took uncoated bullets from the same bag and used harbor freight red and they coated good it must just be the absolute powder is sensitive to contamination i haven't got it to...

Ok must had been a contamination problem cleaned them in acetone and reshot them coating came out good i hammered out a new and old 218589

Oven temp is good checked it. It is flaking off where it is sized but its only on my 9mm and 300 blackout bullets my 9mm and 40cal were cast cooled stored and baked together but it fails on 9mm...

Hello all. I got some absolute powder neon green it shoots on good but not the prettiest using shake and bake but i can't get it to keep from flaking off after sizing i have tried under/ over...

The hardest bullets i have ran through it have been straight cww think it was 12bhn but if i push them faster the 1600-1700 haven't had time to set up the crony the accuracy is gone thats my i took...

It went up in flamesabout 3'tall but i was out in the open and my stainless spoon is about 3' long so i just stir it in let it flash and burn off the wax ring fluxed alot better then the candles i...

It was 80% dissolved befor i add the first 2 # of tin but there was a small amount of tin in the lead pipe solder joints so that may have played apart in it

After ordering the antimony i have been stressing over after reading all the headaches people had with it and i wasn't a problem at all would have went faster if i broke it up but all i did was...

I ended up going 60# pure 10#superhard and 4# tin bullets water dropped at 20 bhn 8 minutes after castmaybe +-on bhn mixed it after a 12hr shift and a pot of coffee hard to hold the lee scope...

In tulsa its .60cents a pound for mixed wheel weights if your a reg customer they will sale to you for .40 out of a 50#bucket i got 15# of lead after that i just get superhard to blend with my horde...

I have over a 1000# of mostly pure lead some tin from solder joints i used the rotometal superhard on my last batch at 60# pure 10# superhard and 4# tin and its putting out a bullet at 20bhn waterd...

hello all my buy it now got the best of me and I got 10#s of pure antimony chunks and 10 #s of tin that will be here tomorrow shooting for a 90-5-5 alloy 100# batches whats the best approach to...

This was what i got poured out last weekend around 400# of lead pipe 197597

Thanks everyone for the replys my alloy and freechex 3 was delivered today now i need an arborpress ans aluminum flashing the right thickness and ill be set up

Hello all been looking at old post on the super hard alloy i have about 1000# of soft lead bhn of 5-8 and around 8# of tin i have 10#of super hard on the way whats the best mix ratio to get a 15+...

I have ran into a few 100 9mm case of range brass that my lee sizing die would leave a step and be galded at the base but i could run it in my rcbs die and it would fix them and after fighting stuck...

I have around 600# of lead pipe to melt down if it will stop raining in Oklahoma build a new outdoor firebox to heat my shop with a drop in 12"×15" pot

I have done everthing i can think of to do andcant get rid of the small ding in the nose thought it was ramping up and hitting the top of the chamber but come to the conclusion its hitting the feed...

I think i got it figured out if you ease the bcg home the round jumps up really sharp into the chamber dinging the nose and i think i may have to sand down my case holder to set my shoulder back...

The upper is a saa. M4 feed ramps is what it has on the website accuracy with one load of 12.5gr of h110 was about 1.5" but i was having to pogo the gun off the shooting bench so much extracting...

The bullets are sized to 309 the outside of the case neck is running. 330-.333. I sized the brass with rcbs sb dies and i didn't use the lee factory crimp die the badly dinged rounds is feeding...

Ok i worked up 9 loads with 1680 rl7 and h110 my problems started on round 2 with it not chambering all the way my col was 1.970+-5 the nose of bullet is hitting hard ramping into the chamber and...

Well went to my favorite tulsa reloading shop no go on the new ar reloading handbook sold out so got it on its way from amazon but got a spare lee trimmer Guage and a quick trim die and 100 gas...

Thanks again everyone for the help ill pickup a new manual to add to the 15 i already have . After my dad ruptured a case in his 338 lapua mag (used Hornady mid range data with i think a nosler ...

Thanks everyone for the replys ill get a new lyman manual and check out that johnnys reloading bench on YouTube been watching alot of Elvis ammo on there after i get the 300blackout reloading...