I have a couple of loads for my M95/34, both of them 1.5" or less (5 shots) @ 50 yds:
1. Steel 21gr
2. Duplex load: A5744 11gr + WC867 27gr + PSB to fill the case
My alloy is WW with some extra...

Not sure if this will help you, but I've played a bit with surplus WC867 (new powder for Wideners). I've heard this is quite close to WC872, so it may apply to some degree...
Most of my work was...

Rifle: K31 scoped (scout); Range: 50 yards, bench rest
Boolit: Lee 155 gr., blue PC, Hornady GC, sized to .310" after coating
Alloy: close to lyman #2 @ 14 BHN (WW with some SuperHard and Tin...

Gave this coating material a try. Painted some lee 155 boolits (2 coats), put GC's on them and went to the range (50 yards). Main purpose was to see if there is any difference in different GC...

+1
PC coating gives you a nice, harder than lead alloy shell, but it's only about .002" thick and does nothing (or very little, that is) to improve your boolit toughness.

Will this lube work on rifle velocities 1800 to 2000 fps? Does it require tumble lube boolit design?

Citric acid (Lemishine, etc) is obviously an acid...Dawn is an alkaline solution. I keep seeing recipes where both are in the mix, don't they neutralize each other? Citric acid will help clean the...

Turpentine does the same thing to HFPC red...but it stinks like hell!

Here's a picture of what I used, the can said it's tintable white, but it was actually gray. It's a 2 part epoxy and I mixed it 1:1. I don't remember where I bought it from (might have gotten it from...

Hammer smash test done. Used a 2.5 lbs. hammer and hit them quite hard (my alloy is about 13 BHN). Top ones are epoxy floor paint and bottom are HFPC black (used lacquer thinner on this batch, but...

I used both, acetone and lacquer thinner, I don't really see any significant difference...

That is pretty slick, I bet you'll get some nicely coated pils...I went away from using a PC gun because the process it's too laborious, given all the set up and cleaning required. Plus no matter how...

I'll find out when I'll have a chance to shoot them (which won't happen for a while), but I don't expect any complications. The amount left of the bullet is next to nothing and additionally I'll gas...

Not really, on the contrary,it is often used as a dry lubricant...
http://www.eurotalc.eu/functionsapplication.html

Just did a couple of batches today (piglet method). First, I used some gray 2 part floor epoxy paint which coated nice, only one coat seems to be enough (adds about .002" to the diameter). Second I...