if i had range scrap, i would use only that. i've been using a 50/50 mix of WW to pure for all my powder coating bullets in pistol cal's up to the 500mag.
if i had range scrap, i would use only that. i've been using a 50/50 mix of WW to pure for all my powder coating bullets in pistol cal's up to the 500mag.
But my range scrap has only something about 10 BHN (pencil tested) and thatīs so low for that caliber (for 9mm is advised something about 16 or 17 BHN as minimum) especially with polygonal rifling (G 17).
It is true that iīll be loading this to a lot slower velocities than standard 9mm is (155 will be about 860 ft/s and 147 about 960 - 980 ft/s). And plus for that is, that this bullets has longer leading surface than standard 115 or 124 gn ones.
But itīs little unusual using this soft lead for that type of loads.
Will powder coat make that big difference?
Thanks
Finally got a mold and got some cast and coated with hi tek copper
Great looking bullets!
Hey all - I realize this is closed, but any chance there are any more of the 147s? I would kill for one!
Many thanks and sorry to bother if not.
I'm also REALLY late to this party!! Maybe Miha would consider a rerun of this mold? I would like one!
We need a honcho for re-run....
Honcho gets free mold.... :)
Ill be the honcho, (ive bought enough molds from you recently) what is it that this person actually does? Is this the "herding cats" job? 🤣Quote:
Originally Posted by MiHec
Sent from my SM-G920V using Tapatalk
You should open new thread in active group buy section and make a list of people.Quote:
Originally Posted by Lakehouse2012
You can copy paste original text from 1st post (pictures, too). Prices are the same (and options) with 15% off on group buy