Originally Posted by
Dr3wcifer
Take a breather, I asked an honest question. You said in your initial comment that you weren't sure it contained zinc, but you fluxed with sulfur anyway, so I was honestly wondering why...
I offered a reasonable test of whether zinc could be removed from a lead alloy with sulfur with measurements and reproducible tests. I recorded and posted it so that people could potentially learn something helpful about whether or not sulfur is something worth trying. My data showed that sulfur can remove zinc. You came into this discussion with your story about how you tried it once on an alloy that may or may not have had zinc in it and it was "BAD BAD BAD BAD." You offered nothing to the discussion other than an unhelpful personal story about why you don't like it. But you ended with a comment about how an XRF study of the alloy showed no zinc...
If you would like to contribute something helpful to the discussion, feel free. Otherwise, please ignore this post.