I mark the BHN on my ingots and store accordingly in my 2 ingots deep shelf unit.
https://i.imgur.com/a1oaQV6.jpg
I cast my pewter into .5 oz boolits for easier alloying and "sweetening" my casting pot
https://i.imgur.com/gHoM3nZ.jpg
https://i.imgur.com/gKCxmL5.jpg
https://i.imgur.com/H8sDFJC.jpg
GRMPS,
Since I just came into approximately 22 lbs. of pewter, this week, that I have yet to melt out. And would like to do as you are, 1/2 ounce size pieces or so. What ratio do you add to your pot to “sweeten” the mix?
.....
Just some various shapes for different alloys.
I also use a letter/number set to punch each ingot with contents...PEW/RL/WW/PB...etc.
redhawk
Attachment 266804Attachment 266800Attachment 266801
I wanted to get through my smelting pot quicker in order to shorten the time to process my stock of casting lead so that lead (ha, ha) me to looking for a larger mold. Wilton had the perfect mold for me. Each "BRICK" is about 10 pounds and allows me to empty a pot quickly and they still fit and melt quickly in my Master Caster too.
https://i.postimg.cc/9Q9B8wXq/20190325-043025.jpg
https://i.postimg.cc/k5ntQ22C/Screen...9-06-53-35.png
I have exactly those same quadruple loaf molds.
Too big for my own pots, but practical for bulk storage of source metals. The final alloy, when made up, is poured into CastBoolit molds.
It's purpose built.
I had to laugh at this one...how do you make a "Glamor Shot" out of a pile of lead??
What??
Well, beauty is in the eye of the beholder, and I have to concede some photos are well composed and nicely done.
For my own case, if mass makes class, and too many dusty and neglected ingot buckets of lead biscuits and corncobs makes you drool, perhaps I should enter a snapshot too.
Pablo